Essential oils (EO) have diverse applications, such as antibacterial and antifungal activity. However, they are susceptible to oxidation in the presence of air, light, and moisture. In addition, they are thermally unstable. In this sense, it is necessary to develop techniques to increase the lifespan of EO. In this work, EO was obtained from cloves and characterized by different techniques. The major compounds found were eugenol (83%), eugenol acetate (9%), and β-caryophyllene (8%). The EO was encapsulated by extrusion using a microfluidic device. The sodium alginate was used as wall material, and the CaCl2 solution was used as a crosslinking agent. The microcapsule presented sizes of 164.7 ± 0.3 μm, with an encapsulation yield of 64 ± 14%. Functional characteristic groups of EO were observed in the microcapsule by infrared and Raman spectroscopies. The microcapsule increased the thermal decomposition of the EO from 162 to 230 °C. Release kinetics of the capsule was performed, with an equilibrium time of 72 h and release of 54% of the EO. Finally, the pure EO and encapsulated EO-microcapsules were applied in the Aedes aegypti larvae control, showing mean lethal concentration necessary to eliminate 50% (LC50) values of 74.4 and 96.9 μg mL-1 and lethal concentration necessary to eliminate 90% (LC90) of 106.2 and 133.3 μg mL-1 for pure EO and encapsulated EO, respectively. Therefore, it was concluded that these microcapsules have the potential for application in the Aedes aegypti larvae control.

In this work, cellulose-based composite biofilms doped with silver nanoparticles (AgNPs) have been produced by eco-friendly process. The AgNPs were synthesized from Ilex paraguariensis with an average size of 45 nm, a characteristic plasmon band at 450 nm and zeta potential of -23 mV. The biofilm has been synthesized by casting method, using different volumes of AgNPs suspension with glycerol plasticizing agent (T6-T10) or not (T1-T5). The AgNPs were successfully incorporated into the biofilms, which was confirmed by scanning electron microscopy. The mechanical and optical structural and the antimicrobial properties of the biofilms have been determined. In the presence of AgNPs, the mechanical properties, thermal stability and water vapor barrier of the biofilms have not been altered. However, the addition of glycerol decreased the tensile strength and the modulus of elasticity, in addition to increasing the elongation of the biofilms and the water vapor barrier. The biofilm T10 showed a transmittance of ca. 10%, with high potential to be used as a UV light blocker. Finally, the biofilms doped with AgNPs showed activity against the bacterium Pseudomonas fluorescens. Given the above, this work presented a new biofilm with activity against the bacterium Pseudomonus fluorescens obtained by eco-friendly process.